Microwave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation

Document Type : Reasearch Paper

Authors

• Sadigheh Bazgir
• Saeed Farhadi

Department of Chemistry, Lorestan University, Khoramabad 68151-44316, Iran.

Abstract

In this work, Co₃O₄ nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC₂O₄.2H₂O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co₃O₄ nanorods were fully characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet–visible spectroscopy (UV–Vis), energy-dispersive X-ray spectroscopy (EDX), and magnetic measurements. TEM and SEM images showed that the Co₃O₄ nanorods have a length of 1-3 µm and diameter of 40-80 nm. FT-IR, XRD, EDX and selected-area electron diffraction demonstrated that the nanorods are composed of pure cubic phase Co₃O₄. Magnetic measurements at room temperature suggested the existence of a weak ferromagnetic behavior. The optical spectrum indicated two direct band gaps at 2.20 and 3.60 eV with a blue shift compared with the bulk sample. The photocatalytic activity of Co₃O₄ nanorods was investigated for the degradation of methylene blue (MB) as a model of dye pollutants in the presence of H₂O₂ as a green oxidant. The Co₃O₄ nanorods showed high efficiency for the degradation of MB dye by using H₂O₂ under visible light irradiation. Trapping experiments indicated that hydroxyl (^•OH) radicals were the main reactive species for dye degradation in the present photocatalytic system. In addition, the possible photodegradation mechanism was also proposed based on the trapping experiment results.

Keywords

• Co3O4 nanorods
• Methylene blue dye
• Microwave irradiation
• Photocatalytic degradation
• Transition metal oxides

20.1001.1.20088868.2017.8.4.2.5

Main Subjects

• Nanocatalyst
• Nanochemistry
• Nanostructured Materials

---

References

[1] Klabunde K. J., Richards R. M., (2012), Nanoscale Materials in Chemistry. 2nd edn. Wiley, New York.

[2] Mate V. R., Shirai M., Rode C. V., (2013), Heterogeneous Co₃O₄ catalyst for selective oxidation of aqueous veratryl alcohol using molecular oxygen. Catal. Commun. 33: 66–69.

[3] Warang T., Patel N., Santini A., Bazzanella N., Kale A., Miotello, A, (2012), Pulsed laser deposition of Co₃O₄ nanoparticles assembled coating: Role of substrate temperature to tailor disordered to crystalline phase and related photocatalytic activity in degradation of methylene blue. Appl. Catal. A: Gen. 423–424: 21– 27.

[4] Casas-Cabanas M., Binotto G., Larcher D., Lecup A., Giordani V., Tarascon, J. M., (2009), Defect chemistry and catalytic activity of nanosized. Co₃O₄. Chem. Mater. 21: 1939–1947.

[5] Askarinejad A., Bagherzadeh M., Morsali A, (2010), Catalytic performance of Mn₃O₄ and Co₃O₄ nanocrystals prepared by sonochemical method in epoxidation of styrene and cyclooctene. Appl. Surface Sci. 256: 6678–6682.

[6] Lou X. W., Deng D., Lee J. Y., Feng J., Archer L. A., (2008), Self-supported formation of needlelike Co₃O₄ nanotubes and their application as lithium-ion battery electrodes. Adv. Mater. 20: 258–262.

[7] Chou S. L., Wang J. Z., Liu H. K., Dou S. X., (2008), Electrochemical deposition of porous Co₃O₄ nanostructured thin film for lithium-ion battery. J. Power. Sources. 182: 359–364.

[8] Li Y. G., Tan B., Wu Y. Y., (2008), Mesoporous Co₃O₄ nanowire arrays for lithium ion batteries with high capacity and rate capacity. Nano Lett. 8: 265–270.

[9] Li W.Y., Xu L. N., Chen J., (2005), Co₃O₄ nanomaterials in lithium-ion batteries and gas sensors. Adv. Func. Mater. 15: 851–857.

[10] Sugimoto T., Matijevic E., (1979), Colloidal cobalt hydrous oxides, preparation and properties of monodispersed. Co₃O₄. J. Inorg. Nucl. Chem. 41: 165–172.

[11] Makhlouf S. A., (2002), Magnetic properties of Co₃O₄ nanoparticles. J. Magn. Magn. Mater. 246: 184–190.

[12] Sun L., Li H., Ren L., Hu C., (2009), Synthesis of Co₃O₄ nanostructures using a solvothermal approach. Solid State Sci. 11: 108–112.

[13] Chen Y., Zhang Y., Fu S., (2007), Synthesis and characterization of Co₃O₄ hollow spheres. Mater. Lett. 61: 701–705.

[14] Masoomi M. Y., Morsali A., (2012), Applications of metal-organic coordination polymers as precursors for preparation of nano-materials. Coord. Chem. Rev. 256: 2921-2943.

[15] Mohandes F., Davar F., Salavati-Niasari M., (2010), Preparation of Co₃O₄ nanoparticles by nonhydrolytic thermolysis of [Co(Pht)(H₂O)]_n polymers.  J. Magn. Magn. Mater. 322: 872–877.

[16] Kodge A., Kalyane S., Lagashetty A.,(2012),Synthesis, characterization and thermal study of poly (methyl methacrylate)-Co₃O₄ nanocomposite film. Int. J. Nano Dimens.3: 53-57.

[17] Thangavelu K., Parameswari K., Kuppusamy K., Haldorai Y., (2011), A simple and facile method to synthesize Co₃O₄ nanoparticles from metal benzoate dihydrazinate complex as a precursor. Mater. Lett. 65: 1482–1484.

[18] Salavati-Niasari M., Khansari A., Davar F., (2009), Synthesis and characterization of cobalt oxide nanoparticles by thermal treatment process. Inorg. Chim. Acta. 362: 4937–4942.

[19] Farhadi S., Pourzare K., (2012), Simple and low-temperature preparation of Co₃O₄ sphere-like nanoparticles via solid-state thermolysis of the [Co(NH₃)₆](NO₃)₃ complex. Mater. Res. Bull. 47: 1550–1556.

[20] Farhadi S., K. Pourzare, (2014), Synthesis and characterization of Co₃O₄ nanoplates by simple thermolysis of the [Co(NH₃)₆]₂(C₂O₄)₃·4H₂O complex.Polyhedron. 67: 104–110.

[21] Farhadi S., Nadri Gh., Javanmard M., (2016), [Co(NH₃)₅(NO₃)](NO₃)₂ as an energetic coordination precursor for the preparation of Co₃O₄ nanoparticles at low temperature. Int. J. Nano Dimens. 7: 201-207.

[22] Li L., Chu Y., Liu Y., Song J. L., Wang D., Du X. W., (2008), A facile hydrothermal route to synthesize novel Co₃O₄ nanoplates. Mater. Lett. 62: 1507–1510.

[23] Du J., Chai L., Wang G., Li K., Qian Y., (2008),Controlled synthesis of one-dimensional single-crystal Co₃O₄ nanowires.  Aust.  J. Chem. 61: 153–158.

[24] Wang R. M., Liu C. M., Zhang H. Z., Chen C. P., Guo L., Xu H. B., Yang S. H., (2004), Porous nanotubes of Co₃O₄: Synthesis, characterization and magnetic properties. Appl. Phys. Lett. 85: 2080–2082.

[25] Li Y., Zhao J., Dan Y., Ma D., Zhao Y., Hou S., Lin H., Wang Z., (2011), Low temperature aqueous synthesis of highly dispersed Co₃O₄ nanocubes and their electrocatalytic activity studies. Chem. Eng. J. 166: 428–434.

[26] Sun H., Ahmad M., Zhu J., (2013), Morphology-controlled synthesis of Co₃O₄ porous nanostructures for the application as lithium-ion battery electrode. Electrochim. Acta. 89: 199-205.

[27] Ren M., Yuan S., Su L., Zhou Z., (2012), Chrysanthemum-like Co₃O₄ architectures: Hydrothermal synthesis and lithium storage performances. Solid State Sci. 14: 451-455.

[28] Yang L. X., Zhu Y. J., Li L., Zhang L., Tong H., Wang W. W., (2006), A facile hydrothermal route to flower-like cobalt hydroxide and oxide. Eur. J. Inorg. Chem. 23: 4787–4792.

[29] Jiu J., Ge Y., Li X., Nie L., (2002), Preparation of Co₃O₄ nanoparticles by a polymer combustion route. Mater. Lett. 54: 260–263.

[30] Gu F., Li C., Hu Y., Zhang L., (2007), Synthesis and optical characterization of Co₃O₄ nanocrystals via a facile combustion method. J. Crys. Growth. 304: 369–373.

[31] Gardey-Merino M. C., Palermo M., Belda R., Fernández de Rapp M. E., Lascalea G. E., Vázquez P. G., (2012 ), Combustion synthesis of Co₃O₄ nanoparticles: fuel ratio effect on the physical properties of the resulting powders. Proced. Mater. Sci. 1: 588-593.

[32] Ma J., Zhang S., Liu W., Zhao Y., (2010), Facile preparation of Co₃O₄ nanocrystals via a solvothermal process directly from common Co₂O₃ powder. J. Alloys Compd. 490: 647–651.

[33] Lester E., Aksomaityte G., Li J., Gomez S., Gonzalez-Gonzalez J., Poliakoff, M., (2012), Controlled continuous hydrothermal synthesis of cobalt oxide (Co₃O₄) nanoparticles. Prog. Cryst. Growth Charact. Mater. 58: 3–13.

[34] Baydi M. E., Poillerat G., Rehspringer J. L., Gautier J. L., Koenig J. F., Chartier P., (1994), A sol–gel route for the preparation of Co₃O₄ catalyst for oxygen electrocatalysis in alkaline medium. J. Solid State Chem. 109: 281–288.

[35] Kim D. Y., Ju S. H., Koo H. Y., Hong S. K., Kangf Y. C., (2006), Synthesis of nanosized Co₃O₄ particles by spray pyrolysis. J. Alloys Compd. 417: 254–258.

[36] Kumar R. V., Diamant Y., Gedanken A., (2000), Sonochemical synthesis and characterization of nanometer-size transition metal oxides from metal acetates. Chem. Mater. 12: 2301–2305.

[37] Wang X., Chen X. Y., Gao L. S., Zheng H. G., Zhang Z., Qian, Y. T., (2004), One-dimensional arrays of Co₃O₄ nanoparticles: Synthesis, characterization and optical and electrochemical properties. J. Phys. Chem. B. 108: 16401–16404.

[38] Fan S., Liu X., Li Y., Yan E., Wang C., Liu J., Zhang Y., (2013), Non-aqueous synthesis of crystalline Co₃O₄ nanoparticles for lithium-ion batteries. Mater. Lett. 91: 291–293.

[39] Jiang J., Li L., (2007), Synthesis of sphere-like Co₃O₄ nanocrystals via a simple polyol route. Mater. Lett. 61: 4894–4896.

[40] Zou D., Xu C, Luo H., Wang L., Ying T., (2008),  Synthesis of Co₃O₄ nanoparticles via an ionic liquid-assisted methodology at room temperature. Mater. Lett. 62: 1976–1978.

[41.] Zhou K., Liu J., Wen P., Hu Y., Gui Z., (2015), Morphology-controlled synthesis of Co₃O₄ by one step template-free hydrothermal method.Mater. Res. Bull.67: 87–93.

[42]  Zhu Y. J., Chen F., (2014), Microwave-assisted preparation of inorganic nanostructures in liquid phase. Chem. Rev. 114: 6462–6555.

[43] Kitchen H. J., Vallance S. R.,  Kennedy J. L., Tapia-Ruiz N., Carassiti L., Harrison A.,  Whittaker A. G., Drysdale T. D., Kingman S. W., Gregory D. H., (2014),Modern microwave methods in solid-state inorganic materials chemistry: From fundamentals to manufacturing. Chem. Rev. 114: 1170–1206.

[44] Assi N., Sharif A. M., Naeini, Q. M., (2014), Synthesis, characterization and investigation photocatalytic degradation of Nitro Phenol with nano ZnO and ZrO₂. Int. J. Nano Dimens. 5: 387-391.

[45] Assi N., Sharif A. M., Bakhtiari H., Naeini Q. M., (2014), Photocatalytic property of ZnO and Mn-ZnO nanoparticles in removal of Cibacet Turquoise blue G from aquatic solution. Int. J.  Nano Dimens. 5: 145-154.

[46] Majedi  A., Davar F., Abbasi A. R., (2016), Metal-organic framework materials as nano photocatalyst. Int. J. Nano Dimens. 6: 1-14.

[47] Khodadadeh F., Aberoomand-Azar P., Tehrani M. S., Assi N., (2016), Photocatalytic degradation of, 2, 4, 6-Trichlorophenol with CdS nanoparticles synthesized by a microwave-assisted sol-gel method. Int. J. Nano Dimens. 7: 263-269.

[48] Nakata K., Fujishima A., (2012),  TiO₂ photocatalysis: Design and applications.J. Photochem. Photobiol. C: Photochem. Rev. 13: 169-189.

[49] Janitabar Darzi S., Mahjoub A. R., Bayat A., (2016), Synthesis and characterization of visible light active S-doped TiO₂ nanophotocatalyst. Int. J. Nano Dimens. 7: 33-40.

[50] Abbasi A., Jahanbin-Sardroodi J., (2016), A theoretical study on the adsorption behaviors of ammonia molecule on N-doped TiO₂ anatase nanoparticles: Applications to gas sensor devices. Int. J. Nano Dimens. 7: 349-359.

[51] Rastkar -Ebrahimzadeh A., Abbasi M., Jahanbin Sardroodi J., Afshari S., (2015), Density functional theory study of the adsorption of NO₂ molecule on nitrogen-doped TiO₂ anatase nanoparticles. Int. J. Nano Dimens. 6: 11-17.

[52] Zakeri S. M. E., Asghari M., Feilizadeh M. Vosoughi M., (2014), A visible light driven doped TiO₂ nanophotocatalyst: Preparation and characterization. Int. J. Nano Dimens. 5: 329-335.

[53] Khojasteh, H., Salavati-Niasari, M., Mazhari, M.-P., Hamadanian, M., (2016), Preparation and characterization of Fe₃O₄@SiO₂@TiO₂@Pd and Fe₃O₄@SiO₂@TiO₂@Pd–Ag nanocomposites and their utilization in enhanced degradation systems and rapid magnetic separation. RSC Adv. 6: 78043-78052.

[54] Safajou H., Khojasteh H., Salavati-Niasari M., Mortazavi-Derazkola S., (2017), Enhanced photocatalytic degradation of dyes over graphene/Pd/TiO₂ nanocomposites: TiO₂ nanowires versus TiO₂ nanoparticles. J. Coll. Interf. Sci. 498: 423-432.

[55] Aghabeygi Sh., Zare-Dehnavi M., (2015), Sonosynthesis and characterization of ZrO_2/ZnO nanocomposite, composition effect on enhancing of photocatalytic properties. Int. J. Nano Dimens. 6: 297-304.

[56] Hoseini L., Bagheri-Ghomi A., (2016), Photocatalytic degradaton of Sulfathiazole using nanosized CdO in aqueous solution. Int. J. Nano Dimens. 8:  159-163.

[57] Azar-Bagheri Gh., Ashayeri V., Mahanpoor K., (2013),  Photocatalytic efficiency of CuFe₂O₄ for photodegradation of acid red 206. Int. J. Nano Dimens. 4: 111-115.

[58] Assi N., Aberoomand-Azar P., Tehrani M. S., Husain S. W.,  Darwish M., Pourmand S., (2017), Synthesis of ZnO-nanoparticles by microwave assisted sol-gel method and its role in photocatalytic degradation of food dye Tartrazine (Acid Yellow 23). Int. J. Nano Dimens. 8: 241-249.

[59]Wang Y., Zhou L., Duan X., Sun H., Tin E. L., Jin W., Wang S., (2015), Photochemical degradation of phenol solutions on Co₃O₄ nanorods with sulfate radicals.  Catal.Today. 25: 576-584.

[60] Qiu X. P., Yu J. S., Xu H. M., Chen W. X., Hu W., Chen G. L., (2016), Interfacial effects of the Cu₂O nano-dots decorated Co₃O₄ nanorods array and its photocatalytic activity for cleaving organic molecules. Appl. Surf. Sci. 382: 249-259.

[61] Lai, T.-L., Lai, Y.-L., Lee, C.-C., Shu, Y.-Y., Wang, C.-B., (2008), Microwave-assisted rapid fabrication of Co₃O₄ nanorods and application to the degradation of phenol. Catal. Today. 131: 105-110.

[62] Gasparotto A., Barreca D, Bekermann D., Devi A.,  Fischer R. A.,  Fornasiero P., Gombac V.,  Lebedev O. I., Maccato C., Montini T.,  Tendeloo G. V., Tondello E., (2011), F-Doped Co₃O₄ photocatalysts for sustainable H₂ generation from water/ethanol. J. Am. Chem. Soc. 133: 19362–19365.

[63] Salavati-Niasari M., Mir N., Davar F., (2009), Synthesis and characterization of Co₃O₄ nanorods by thermal decomposition of cobalt oxalate. J. Phys. Chem. Solids. 70: 847–852.

[64] Nakamoto K., (2009), Infrared and Raman spectra of inorganic and coordination compounds, Part B: Applications in coordination, organometallic and bioinorganic chemistry, 6th edn. Wiley, New York.

[65] Ai L. H., Jiang J., (2009), Rapid synthesis of nanocrystalline Co₃O₄ by a microwave-assisted combustion method. Powder Tech. 195: 11–14.

[66] Bhatt A. S., Bhat D. K., Tai C. W., Santosh M. S., (2011), Microwave-assisted synthesis and magnetic studies of cobalt oxide nanoparticles. Mater. Chem. Phys. 125: 347–350.

[67] Klug H. P., Alexander L. E., (1964), X-ray Diffraction Procedures, 2nd edn. Wiley, New York.

[68] Nethravathi C., Sen S., Ravishankar N., Rajamathi M., Pietzonka C., Harbrecht B., (2005), Ferrimagnetic nanogranular Co₃O₄ through solvothermal decomposition of colloidally dispersed monolayers of α-cobalt hydroxide. J. Phys. Chem. B. 109: 11468 –11472.

[69] Ichiyanagi Y., Kimishima Y., Yamada S., (2004), Magnetic study on Co₃O₄ nanoparticles. J. Magn. Magn. Mater. 272–276: e1245–e1246.

[70] Ozkaya T., Baykal A., Toprak M. S., Koseoglu Y, Durmus Z., (2009), Reflux synthesis of Co₃O₄ nanoparticles and its magnetic characterization. J. Magn. Magn. Mater. 321: 2145–2149.

[71] He T., Chen D. R., Jiao X. L., Wang Y. L., Duan Y. Z., (2005),  Solubility-controlled synthesis of high-quality Co₃O₄ nanocrystals. Chem. Mater. 17: 4023–4030.

[72] Gulino A., Dapporto P., Rossi P., Fragala I., (2003), A novel self-liquid MOCVD precursor for Co₃O₄ thin films. Chem. Mater. 15: 3748–3752.

[73] Yu K., Yang S., Liu C., Chen H., Li H., Sun C., Boyd S. A., (2012), TiO₂-assisted photodegradation of dyes. 9. Photooxidation of a squarylium cyanine dye in aqueous dispersions under visible light irradiation. Environ. Sci.Technol. 46: 7318–7326.

[74] Zhang H., Lv X., Li Y., Wang Y., Li J., (2010), P25-Graphene composite as a high performance photocatalyst. ACS Nano. 4: 380–386.