Synthesis and characterization of Titanium Dioxide modified zeolite-x based composite: To study the solar cell application

Document Type : Reasearch Paper

Authors

• Ramkumar Singh Dandolia ¹
• Shatrughan Singh Tomar ²
• Arvind Dandotia ¹
• Radha Tomar ³
• Rajendra K. Tiwari ¹

¹ School of Studies in Physics, Jiwaji University, Gwalior-474011, India.

² Govt. SLP PG College, Morar, Gwalior-474006, India.

³ School of Studies in Chemistry, Jiwaji University, Gwalior-474011, India.

10.22034/ijnd.2022.1957706.2141

Abstract

This paper focuses on the performance of introducing zeolite nanocomposite into photoanodes of dye-sensitized solar cells. Mesoporous titanium dioxide and zeolite nanoparticles were synthesized using hydrothermal technique. The Synthesized nanocomposite was characterized by various techniques via X-ray diffraction technique, Scanning electron microscopy, and Ultraviolet visible spectrophotometer. XRD analysis showed highly crystalline zeolite, Titanium oxide and its composite showed polycrystalline nature. SEM results elucidated that the incorporation of Titanium oxide into zeolite changed the surface morphology from rectangular to spherical.  Ultraviolet visible spectroscopy shows that the bandgap of zeolite, titanium oxide, and its composite is 3.4, 3.2, and 4.14 eV, respectively. Current voltage results confirmed the formation of p-n heterojunction formed between p– and n-type materials indicating the behavior of solar cell devices.

Keywords

• Composite
• SEM
• Synthesis
• Titanium Oxide
• Zeolite

20.1001.1.20088868.2022.13.4.8.6

---

References

[1] Ahmad M. S., Pandey A. K., Abd Rahim N., (2017), Advancements in the development of TiO₂ photoanodes and its fabrication methods for dye sensitized solar cell (DSSC) applications. A review. Renew. Sust. Energ. Rev. 77: 89-108.

[2] So S., Hwang I., Schmuki P., (2015), Hierarchical DSSC structures based on “single walled” TiO₂ nanotube arrays reach a back-side illumination solar light conversion efficiency of 8%. Energy Environ. Sci. 8: 849-854.

[3] John K. A., Naduvath J., Remillard S. K., Shaji S., DeYoung P. A., Kellner Z. T., Philip R. R., (2019), A simple method to fabricate metal doped TiO₂ nanotubes. Chem. Phys. 523: 198-204.

[4] Xie K., Guo M., Liu X., Huang H., (2015), Enhanced efficiencies in thin and semi-transparent dye-sensitized solar cells under low photon flux conditions using TiO₂ nanotube photonic crystal. J. Power Sources. 293: 170-177.

[5] Wang H., Liu Q., Liu D., Su R., Liu J., Li Y., (2018), Computational prediction of electronic and photovoltaic properties of anthracene-based organic dyes for dye-sensitized solar cells. Int. J. Photoenergy. 2018: Article ID: 4764830.

[6] Halme J., Vahermaa P., Miettunen K., Lund P., (2010), Device physics of dye solar cells. Adv. Mat. 22: E210-E234.

[7] Tsvetkov N., Larina L., Ku Kang J., Shevaleevskiy O., (2020), Sol-gel processed TiO₂ nanotube photoelectrodes for dye-sensitized solar cells with enhanced photovoltaic performance. Nanomater. 10: 296-302.

[8] O'regan B., Grätzel M., (1991), A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO₂ films. Nature. 353: 737-740.

[9] Yahya M., Bouziani A., Ocak C., Seferoğlu Z., Sillanpää M., (2021), Organic/metal-organic photosensitizers for dye-sensitized solar cells (DSSC): Recent developments, new trends, and future perceptions. Dyes Pigm. 192: 109227.

[10] Yu J., Fan J., Lv K., (2010), Anatase TiO₂ nanosheets with exposed (001) facets: Improved photoelectric conversion efficiency in dye-sensitized solar cells. Nanoscale. 2: 2144-2149.

[11] Hafez H., Lan Z., Li Q., Wu J., (2010), High efficiency dye-sensitized solar cell based on novel TiO₂ nanorod/nanoparticle bilayer electrode. Nanotechnol. Sci. Appl. 3: 45-49.

[12] Nazeeruddin M. K., Kay A., Rodicio I., Humphry-Baker R., Müller E., Liska P., Grätzel M., (1993), Conversion of light to electricity by cis-X₂bis (2, 2'-bipyridyl-4, 4'-dicarboxylate) Ruthenium (II) charge-transfer sensitizers (X= Cl-, Br-, I-, CN-, and SCN-) on nanocrystalline titanium dioxide electrodes. J. Am. Chem. Soc. 115: 6382-6390.

[13] Mora-Sero I., Giménez S., Fabregat-Santiago F., Gómez R., Shen Q., Toyoda T., Bisquert J., (2009), Recombination in quantum dot sensitized solar cells. Acc. Chem. Res. 42: 1848-1857.

[14] Grätzel M., (2005), Solar energy conversion by dye-sensitized photovoltaic cells. Inorg. Chem. 44: 6841-6851.

[15] Yildiz Z. K., Atilgan A., Atli A., Özel K., Altinkaya C., Yildiz A., (2019), Enhancement of efficiency of natural and organic dye sensitized solar cells using thin film TiO₂ photoanodes fabricated by spin-coating. J. Photochem. Photobiol. A. 368: 23-29.

[16] Gnida P., Jarka P., Chulkin P., Drygała A., Libera M., Tański T., Schab-Balcerzak E., (2021), Impact of TiO₂ nanostructures on dye-sensitized solar cells performance. Mater. 14: 1633-1637.

[17] Kathirvel S., Chen H. S., Su C., Wang H. H., Li C. Y., Li W. R., (2013), Preparation of smooth surface TiO₂ photoanode for high energy conversion efficiency in dye-sensitized solar cells. J. Nanomater. 2013: Article ID 367510.

[18] Tsai J. K., Hsu W. D., Wu T. C., Meen T. H., Chong W. J., (2013), Effect of compressed TiO₂ nanoparticle thin film thickness on the performance of dye-sensitized solar cells. Nanoscale Res. Lett. 8: 1-6.

[19] Tong Z., Peng T., Sun W., Liu W., Guo S., Zhao X. Z., (2014), Introducing an intermediate band into dye-sensitized solar cells by W6+ doping into TiO₂ nanocrystalline photoanodes. The J. Phys. C. 118: 16892-16895.

[20] Kakiage K., Aoyama Y., Yano T., Otsuka T., Kyomen T., Unno M., Hanaya M., (2014), An achievement of over 12 percent efficiency in an organic dye-sensitized solar cell. Chem. Comm. 50: 6379-6381.

[21] Graetzel M., Janssen R. A., Mitzi D. B., Sargent E. H., (2012), Materials interface engineering for solution-processed photovoltaics. Nature. 488: 304-312.

[22] Mariotti N., Bonomo M., Fagiolari L., Barbero N., Gerbaldi C., Bella F., Barolo C., (2020), Recent advances in eco-friendly and cost-effective materials towards sustainable dye-sensitized solar cells. Green Chem. 22: 7168-7218.

[23] Yeoh M. E., Chan K. Y., (2017), Recent advances in photo‐anode for dye‐sensitized solar cells: A review. Int. J. Energy Res. 41: 2446-2467.

[24] Scarabino S., Nonomura K., Vlachopoulos N., Hagfeldt A., Wittstock G., (2020), Effect of TiO₂ photoanodes morphology and dye structure on dye-regeneration kinetics investigated by scanning electrochemical microscopy. Electrochem. 1: 329-343.

[25] Leung D. Y., Fu X., Wang C., Ni M., Leung M. K., Wang X., Fu X., (2010), Hydrogen production over titania‐based photocatalysts. Chem. Sus. Chem. 3: 681-694.

[26] Liu G., Gong J., Kong L., Schaller R. D., Hu Q., Liu Z., Xu T., (2018), Isothermal pressure-derived metastable states in 2D hybrid perovskites showing enduring bandgap narrowing. Proc. Natl. Acad. Sci. 115: 8076-8081.

[27] Hutter E. M., Sutton R. J., Chandrashekar S., Abdi-Jalebi M., Stranks S. D., Snaith H. J., Savenije T. J., (2017), Vapour-deposited cesium lead iodide perovskites: Microsecond charge carrier lifetimes and enhanced photovoltaic performance. ACS Energy Lett. 2: 1901-1908.

[28] Wang X., Li Z., Shi J., Yu Y., (2014), One-dimensional titanium dioxide nanomaterials: Nanowires, nanorods, and nanobelts. Chem. Rev. 114: 9346-9384.

[29] Ooyama Y., Harima Y., (2012), Photophysical and electrochemical properties, and molecular structures of organic dyes for dye‐sensitized solar cells. Chem. Phys. Chem. 13: 4032-4080.

[30] Alfanaar R., Elim P. E., Yuniati Y., Kusuma H. S., Mahfud M., (2021), Synthesis of TiO2/ZnO-anthocyanin hybrid material for dye sensitized solar cell (DSSC). In IOP Conf. Series: Mater. Sci. and Eng. 1053: 012088.

[31] Cejka J., Van Bekkum H., Corma A., Schueth F., (2007), Introduction to zeolite molecular sieves. Elsevier.

[32] Corma A., Zones S., Cejka J., (Eds.), (2010), Zeolites and catalysis: synthesis, reactions and applications. John Wiley & Sons.

[33] Kulprathipanja S., (Ed.) (2010), Zeolites in industrial separation and catalysis. John Wiley & Sons.

[34] Naikoo R. A., Bhat S. U., Mir M. A., Tomar R., Khanday W. A., Dipak P., Tiwari D. C., (2016), Polypyrrole and its composites with various cation exchanged forms of zeolite X and their role in sensitive detection of carbon monoxide. RSC Adv. 6: 99202-99210.

[35] Li W., Liang R., Hu A., Huang Z., Zhou Y. N., (2014), Generation of oxygen vacancies in visible light activated one-dimensional iodine TiO₂ photocatalysts. RSC Adv. 4: 36959-36966.

[36] Sun Y., Lei J., Wang Y., Tang Q., Kang C., (2020), Fabrication of a magnetic ternary ZnFe₂O₄/TiO₂/RGO Z-scheme system with efficient photocatalytic activity and easy recyclability. RSC Adv. 10: 17293-17301.

[37] Back S., Kim J. H., Kim Y. T., Jung Y., (2016), Bifunctional interface of Au and Cu for improved CO₂ electroreduction. ACS Appl. Mater. Interf. 8: 23022-23027.

[38] Rahman A., Nurjayadi M., Wartilah R., Kusrini E., Prasetyanto E. A., Degermenci V., (2018), Enhanced activity of TiO₂/Natural zeolite composite for degradation of methyl orange under visible light irradiation. Int. J. Technol. 9: 1159-1167.